Vacuum furnace is widely used in modern industrial production, but for his skill in vacuum heat treatment is a lot of people don't understand. Our company is a high technology, strength after induction heating equipment suppliers, is willing to work with everyone together to discuss this problem today.
1. Vacuum furnace active connection parts are all made of type O rubber ring sealing connection, this part is cooled.
2. The vacuum furnace processing of titanium alloy, unfavorable use nitrogen as cooling gas, because titanium and nitrogen reaction at high temperature, forming the golden titanium nitride.
3. Vacuum tempering furnace should have fast cooling device. Cooling water pressure should be greater than 0.2 Mpa, the flow should be adjustable.
4. Vacuum furnace maintenance should be in the condition of vacuum or pure nitrogen inflator, avoid inspiratory when not in use at ordinary times, moisture absorption.
5. The domestic vacuum furnace pressure increase rate should be no greater than 1.33 Pa/h, some enterprises abroad standard Pa 0.67 / h
6. Vacuum heating is given priority to with radiation, should keep distance between artifacts in the oven.
7. In the process of heating workpiece and furnace material will be deflated, resulting in a vacuum.
8. Vacuum tempering, vacuum annealing, vacuum heating of vacuum solid solution treatment and aging temperature generally the same as the conventional heating temperature when processing.
9. The workpiece quenching under a vacuum, vacuum quenching oil should be used, the oil has a lower saturated vapor pressure.
10. The cooling gas: steel generally USES ninety-nine point nine nine five percent purity of nitrogen, nitrogen or argon gas, high temperature alloy with ninety-nine point nine nine nine percent of titanium alloy with ninety-nine point nine nine five percent argon gas.